项目 | Zwick HIP25P Plus |
---|---|
最大冲击能量 | 25J |
夏比摆 | l,4,7.5J |
尺寸 (W×H×D) | 1180× 1170×500 mm |
重量 | 215 kg |
冲击速度 | 2.9 m/s,最高 3.8 m/s |
测试温度 | 室温 |
测试标准 | ISO 179 ASTM 06110 |
标准要求 | HIT 5P | HIT 5.5P | HIT 25P | HIT 50P | ||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
方法 | 标准 | 摆锤能量 J |
ft lbf | 冲击时的速度 m/s |
独立 | PC | 独立 | PC | 独立 | PC | 独立 | PC |
夏比 | ISO 179 | 0.5 | 0.37 | 2.9m/s (±10%) | ● | ● | ● | ● | ● | ● | ● | ● |
1 | 0.74 | ● | ● | ● | ● | ● | ● | ● | ● | |||
2 | 1.48 | ● | ● | ● | ● | ● | ● | ● | ● | |||
4 | 2.95 | ● | ● | ● | ● | ● | ● | ● | ● | |||
5 | 3.69 | ● | ● | ● | ● | ● | ● | ● | ● | |||
7.5 | 5.53 | 3.8m/s (±10%) | - | - | - | - | ● | ● | ● | ● | ||
15 | 11.1 | - | - | - | - | ● | ● | ● | ● | |||
25 | 18.4 | - | - | - | - | ● | ● | ● | ● | |||
50 | 36.9 | - | - | - | - | - | - | ● | ● | |||
ASTM D6110 | 0.5 | 0.37 | 大约 3.46m/s | - | - | ● | ● | ● | ● | ● | ● | |
1 | 0.74 | - | - | ● | ● | ● | ● | ● | ● | |||
2.7 | 2 | - | - | ● | ● | ● | ● | ● | ● | |||
5.4 | 4 | - | - | ● | ● | ● | ● | ● | ● | |||
10.8 | 8 | (跌落高度:610±2mm) | - | - | - | - | ● | ● | ● | ● | ||
21.6 | 16 | - | - | - | - | ● | ● | ● | ● | |||
艾氏冲击和“无缺口悬臂梁冲击” | ISO 180 | 1.0 | 0.74 | 3.5m/s (±10%) | - | - | ● | ● | ● | ● | ● | ● |
2.75 | 2.03 | - | - | ● | ● | ● | ● | ● | ● | |||
5.5 | 4.06 | - | - | ● | ● | ● | ● | ● | ● | |||
11 | 8.11 | - | - | - | - | ● | ● | ● | ● | |||
22 | 16.2 | - | - | - | - | ● | ● | ● | ● | |||
ASTM D256/ D 4812 | 1.0 | 0.74 | 大约 3.46m/s | - | - | ● | ● | ● | ● | ● | ● | |
2.75 | 2.03 | - | - | ● | ● | ● | ● | ● | ● | |||
5.5 | 4.06 | - | - | ● | ● | ● | ● | ● | ● | |||
11 | 8.11 | (跌落高度:610±2mm) | - | - | - | - | ● | ● | ● | ● | ||
22 | 16.2 | - | - | - | - | ● | ● | ● | ● | |||
拉伸冲击 | ISO 8256 - 方法 A | 2.0 | 1.48 | 2.9m/s (±10%) | ● | ● | ● | ● | ● | ● | ● | ● |
4.0 | 2.95 | ● | ● | ● | ● | ● | ● | ● | ● | |||
7.5 | 5.53 | 3.8m/s (±10%) | - | - | - | - | ● | ● | ● | ● | ||
15.0 | 11.1 | - | - | - | - | ● | ● | ● | ● | |||
25.0 | 18.4 | - | - | - | - | ● | ● | ● | ● | |||
50.0 | 36.9 | - | - | - | - | - | - | ● | ● | |||
拉伸冲击 -“头部拉伸”法 | ISO 8256 - 方法 B | 2.0 | 1.48 | 2.9m/s (±10%) | - | - | ● | ● | ● | ● | ● | ● |
4.0 | 2.95 | - | - | ● | ● | ● | ● | ● | ● | |||
7.5 | 5.53 | 3.8m/s (±10%) | - | - | - | - | ● | ● | ● | ● | ||
15.0 | 11.1 | - | - | - | - | ● | ● | ● | ● | |||
25.0 | 18.4 | - | - | - | - | ● | ● | ● | ● | |||
50.0 | 36.9 | - | - | - | - | - | - | ● | ● | |||
ASTM D1822 | 2.7 | 2 | 约 3.46m/s(跌落高度:610±2mm) | - | - | ● | ● | ● | ● | ● | ● | |
5.4 | 4 | - | - | ● | ● | ● | ● | ● | ● | |||
10.8 | 8 | - | - | - | - | ● | ● | ● | ● | |||
21.6 | 16 | - | - | - | - | ● | ● | ● | ● | |||
戴恩斯塔冲击 | DIN 53435 | 0.2 | 0.15 | 2.2±0.1m/s | - | - | - | - | - | - | - | - |
0.5 | 0.37 | - | - | ● | ● | ● | ● | ● | ● | |||
1.0 | 0.74 | - | - | ● | ● | ● | ● | ● | ● | |||
2.0 | 1.48 | - | - | ● | ● | ● | ● | ● | ● | |||
4.0 | 2.96 | - | - | ● | ● | ● | ● | ● | ● |